2205 stainless steel i beam
I-beam made of 2205 stainless steel is a high-quality steel product, widely used in the construction industry. It has excellent corrosion resistance and high strength, making it an ideal choice for a variety of applications.
2205 stainless steel is a duplex stainless steel, which means it has a ferrite and austenite structure. This duplex structure provides improved strength and corrosion resistance properties compared to traditional austenitic stainless steels. 2205 stainless steel has good weldability and can be easily welded using standard welding techniques.
The I-beam is a section of steel that is used as a beam in structures to support various loads. It has a wide flange and a narrow web, which provides greater strength and stiffness compared to other types of steel beams. The I-beam is also easier to install and requires less reinforcement compared to other steel beams.
The 2205 stainless steel I-beam is produced according to international standards and undergoes strict quality control to ensure its quality and performance. It is suitable for use in a wide range of applications, including bridges, buildings, offshore platforms, and other structures that require high strength and corrosion resistance.
Compared to traditional carbon steel I-beams, the 2205 stainless steel I-beam has a longer service life and requires less maintenance. It is also safer for the environment because it does not require painting or other types of surface treatment, reducing the amount of environmental pollution associated with these processes.
If you are looking for a high-quality, durable, and corrosion-resistant I-beam for your construction project, the 2205 stainless steel I-beam is an excellent choice. Contact us today to learn more about our products and how they can meet your specific needs.
| Product Name | 2205 stainless steel i beam |
| Material Composition | Chromium (Cr): 21.0 - 28.0% Nickel (Ni): 4.0 - 6.0% Molybdenum (Mo): 1.0 - 3.0% Manganese (Mn): 1.0% maximum Silicon (Si): 1.0% maximum Carbon (C): 0.08% maximum Phosphorus (P): 0.04% maximum Sulphur (S): 0.03% maximum |
| Mechanical Properties | Tensile Strength: ≥ 620 MPa Yield Strength: ≥ 310 MPa Elongation: ≥ 35% in 50mm Reduction of Area: ≥ 55% in 60mm Impact Absorption Energy: ≥ 35 J at -40℃ Hardness: ≤ HB303 |
| Corrosion Resistance Properties | Austenitic Grade: Duplex Stainless Steel Corrosion Resistance: Excellent resistance to chloride corrosion, acids and alkalis. Temperature Resistance: Applicable in a wide range of temperatures, from cryogenic to high temperature. |
| Physical Properties | Specific Heat: ≥ 0.46 kJ/(kg·℃) at 20℃ Thermal Conductivity: ≥ 16 W/(m·℃) at 100℃ Electrical Resistivity: ≥ 1.0 × 10^6 Ω·m at 20℃ |
| Environmental Friendliness | Non-toxic and environmentally friendly, without containing harmful substances such as lead, mercury and cadmium. |